Waldent NanoFill Zirconium Composite Kit

Features

• The material’s high radiopacity ensures that it is easily visible on radiographs, allowing for precise monitoring and assessment of the treatment progress and any underlying dental structures.
• The exceptional wear resistance of the material ensures long-lasting performance and durability, even under the daily stresses of chewing and grinding, reducing the need for frequent replacements or adjustments.
• A high filler load enhances the material’s strength and resilience, providing superior structural integrity and resistance to deformation.
• The material’s packable consistency allows for easy handling and application, ensuring that it can be efficiently placed and shaped.
• The low shrinkage property minimizes changes in volume or shape after curing, which helps maintain the accuracy of the orthodontic appliance and ensures a better fit and comfort for the patient.
• The material’s excellent colour stability ensures that it maintains its aesthetic appearance over time, resisting discoloration and providing a consistent, pleasing look throughout the treatment period.

Description

The NanoFill Zirconium Composite Kit is a high-performance light-cure, radiopaque composite designed for both anterior and posterior dental restorations. This advanced material is ideal for a range of applications, including direct fillings of Class I, II, III, IV, and V cavities in both anterior and posterior teeth.

Its superior physical properties ensure excellent strength, durability, and wear resistance, making it suitable for demanding restorations. The composite features a long working time, allowing clinicians to work efficiently and achieve precise results.

Additionally, it is effective for preventive resin restorations, offering versatility and reliability in various restorative procedures. The NanoFill Zirconium Composite Kit combines aesthetic appeal with functional performance, ensuring high-quality outcomes and patient satisfaction.

Specifications

• Category: Restorative material
• Type: Nanofill zirconium composite kit
• Composition: Bisphenol A Glycidyl methacrylate (Bis-GMA)
  • Urethane Dimethacrylate (UDMA)
  • Bisphenol A diglycidyl methacrylate ethoxylated (Bis-EMA)
• Tensile Strength: 52.4 MPa
• Degree of conversion: 83%
• Flexural modulus: 12.6 GPa
• Shrinkage forces: 0.91 MPa
• Diamond pyramid hardness: 78 kg/mm²
• Thermal expansion coefficient: 22 µm/m°C
• Flexural strength: 85 Mpa
• Compressive strength: 250 Mpa

Packaging

• 7 x 4g Syringe (1xA1, 2xA2,1xA3, 1xA3.5, 1xB2, 1xOA2)
• 1 x 5ml Bottle NanoBond Universal Adhesive
• 1 x 3g Syringe BestEtch
• 4 x Blue Tips (23 gauge)
• Instruction Manual

Direct to Use

• Prepare the tooth: The tooth is first prepared by removing any decay or damaged tissue and cleaning the area.
• Isolate the tooth: The tooth is isolated using a rubber dam or a dental dam to prevent contamination and to keep the tooth dry.
• Apply an adhesive: An adhesive is applied to the prepared tooth surface to bond the composite filling to the tooth structure.
• Place the composite: The NanoFill Zirconium Composite is then placed into the prepared cavity using a hand instrument or a placement instrument. The composite material should be packed firmly and evenly into the cavity to ensure good adaptation and contact with the tooth structure.
• Shape and contour the composite: The composite is shaped and contoured using a dental instrument to achieve the desired anatomical form and occlusal contacts. It is important to ensure that the composite is properly contoured to prevent food accumulation and to promote proper oral hygiene.
• Cure the composite: The composite is then cured using a dental curing light. The curing time depends on the type of composite used and the manufacturer’s instructions.
• Check the bite: After the composite is cured, the bite is checked to ensure that the restoration is not interfering with the patient’s occlusion.
• Polish the composite: The final step is to polish the composite using a dental polishing system to achieve a smooth and shiny surface.