Features
- Dual-functionality: luting and filling capabilities.
- Precise film thickness for accurate restoration.
- Enhanced durability and low stickiness.
- Time-saving with rapid net setting.
- Remineralization promotion for improved longevity.
- Antimicrobial properties for reduced reactions.
Descriptions
VinciSmile Luting-II Glass Ionomer Luting Cement, is a dental product designed for versatile applications in both luting (bonding cement) and filling procedures. This innovative two-in-one solution boasts an ideal film thickness of 12-16 microns, ensuring precise restoration-denture alignment for optimal aesthetic and functional outcomes. VinciSmile Luting-II offers exceptional durability, low stickiness, and time-saving properties, making it a go-to choice for efficient and long-lasting dental restorations. With features such as remineralization promotion, acid resistance enhancement, and antimicrobial properties, this cement prioritizes patient comfort and safety post-procedure. Recommended for various indications including cementation of metal-based and all-ceramic restorations, as well as restoration of caries in unstressed areas, VinciSmile Luting-II is the ideal solution for modern dental practices seeking superior performance and patient satisfaction.
Indications
- Cementation of metal-based inlays, onlays, crowns and bridges.
- Cementation of high strength (zirconia based), all ceramic crowns and bridges.
- Cementation of posts and screws made of metal or high-strength ceramic.
- Cementation of orthodontic bands.
- Restoration of caries in unstressed area.
Advantages
- Good Durability
The higher compression capacity (> 180Mpa) ensures good durability. - When used for luting: Ideal film thickness
- Good durability
- Low stickiness
- Time saving
Specifications
- Powder/Liquid Ratio(g/g): 1.6-1.8/1.0
- Mixing Time: 45s
- Working Time:2min10s
- Setting Time: 3min15s
- Film thickness: 13μm
- Compression Strength: >140Mpa
- Shelf Life: 2 Years
Direction to Use
Tooth Preparation:
- Prepare the tooth following standard procedures.
- Clean the prepared tooth surface with pumice and water.
- Avoid over-drying; use short intervals of water and oil-free air or cotton pellets for drying.
Restoration Preparation:
- Ensure the restoration is pretreated and handled according to the manufacturer’s instructions.
Powder and Liquid Dispensing:
- Use the recommended powder to liquid ratio:
- Luting: 1.6-1.8g powder to 1.0g liquid
- Filling: 2.3-2.5g powder to 1.0g liquid
- Dispense and mix on a pad within the specified time frame.
Mixing:
- Mix the powder and liquid thoroughly within 45 seconds.
- For larger amounts, divide the powder into two equal parts and mix sequentially.
Application for Luting:
- Apply the mixed cement to the prepared tooth/restoration.
- Form the contour during the setting time.
- Finish and polish as needed after setting.
Application for Filling:
- Follow the same mixing procedure as for luting.
- Apply the mixed cement to fill caries or defects.
- Finish and polish after setting.
Working Time and Setting:
- Working time varies based on the application (luting or filling).
- Net setting time ranges from 1 minute 30 seconds to 8 minutes (luting) and 1 minute 30 seconds to 6 minutes (filling) depending on the powder to liquid ratio.
Post-Application:
- For one-visit treatments, adjust contour, finish, and polish after initial set.
- Use standard techniques for finishing and polishing under water spray for standard methods.
Storage and Handling:
- Close bottles immediately after use.
- Store in a cool, dry place away from direct sunlight.
- Use only by dental professionals in recommended indications.
Packaging
- 1 x 30g powder
- 1 x 25g liquid
- 1 x measuring spoon
- 1 x mixing pad